Location » Home » Grades > Special Alloy > Q235 C
Q235 C Application:Engineering and welding
Category Type Steel grade Country
Grades Special Alloy Q235 C China

Chemical composition % of the ladle analysis of grade Q235 C

C(%) Si(%) Mn(%) P(%) S(%) Cr(%) Ni(%) Cu(%)
≤0.18 ≤0.30 0.35~0.80 0.040 0.040 ≤0.30 ≤0.30 ≤0.30

Mechanical properties


The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | ≤ 16:235
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:225
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 40 to 60:215
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:205
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:195
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 150:185

Tensile strength σ b/MPa: 375 ~ 450
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | ≤ 16:26
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:25
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 40 to 60:24
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:23
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:22
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 150:21
Impact test (1) | temperature / ℃ : 0
Impact test (1) | impact absorption power AKV/J: 27 frequency

The cold bending property

Sample direction: horizontal
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | than 60: d = 1.5 a
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 60 ~ 100: d = 2.5 a
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 100 ~ 200: d = 3 a
Mechanical properties of grade Q235 C
Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
916 (≥) 387 (≥) 23 11 44 Solution and Aging, Annealing, Ausaging, Q+T,etc 223
Physical properties of grade Q235 C
Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
942 (≥) 799 (≥) 43 34 11 Solution and Aging, Annealing, Ausaging, Q+T,etc 443
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
153 873 198
Q235 C Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
Y1Cr18Ni9 China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9 China
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3N China
Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
1Cr17Ni7 China
High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc
Y1Cr18Ni9Se China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9 China
Seamless stainless steel tubes for boiler and heat exchanger
00Cr19Ni10 China
Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
1Cr17Mn6Ni5N China
Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc
1Cr18Mn8Ni5N China
Nickel steel, instead of 1cr18ni9
0Cr19Ni9N China
Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components
0Cr19Ni10NbN China
Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES
00Cr18Ni10N China
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12 China
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
0Cr23Ni13 China
Corrosion resistance and heat resistance are better than 0cr19ni9
0Cr25Ni20 China
Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel
0Cr17Ni12Mo2 China
Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Ni12Mo2Ti China
Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2Ti China
Seamless stainless steel tubes for boiler and heat exchanger
A-29 1025 China
General use carbon steel rod
1025 China
These products have been used typically for use in fabrication of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations.

Relevant products

Q235 C Equivalent Grade Stock

Steel grade Dimension Shape Unit Quantity Delivery state Query
SkD-11 Round Bar Stock Φ30-Φ350 Round Bar Kgs 3102 Hot-Rolled+Annealed+black Enquiry
17-4PH Coil Stock 0.08*200mm Coil or Strip Kgs 1623 Cold-Rolled+Annealed Enquiry
D2 Round bar Φ25-Φ380mm Round Bar Kgs 45325 Hot-Rolled+Annealed+black Enquiry
Cr8 flat bar 12*355*L Flat or Square bar Kgs 3965 Forged+Annealed+black Enquiry
17-4PH Round Bar Φ5-300mm*L Round Bar Kgs 46958 Hot-Rolled+Annealed+black Enquiry
17-4PH plate 8-45*1200*3000mm Plate or Sheet Tons 4.9 Hot-Rolled+Annealed+black Enquiry
Cr12MoV 12-160(T)*310-610(W)*L Plate or Sheet Tons 12.38 Hot-Rolled+Annealed+black Enquiry
1.2601 12-160(T)*310-610(W)*L Plate or Sheet Tons 11.22 Hot-Rolled+Annealed+black Enquiry
IncoloyA-286 / GH 2132 Stock Φ8-65mm*L Round Bar Kgs 489 Hot-Rolled+Annealed+black Enquiry
Incoloy800 round bar Φ115*1400 Round Bar Kgs 169 Hot-Rolled+Annealed+black Enquiry
17-7PH / 631 Coil & Strip, Sheet Stock 0.3-3.0*10-180mm Coil or Strip Kgs 1236.22 Cold-Rolled+Annealed Enquiry
X22CrMoV12-1 / 1.4923 Φ17mm Round Bar Kgs 300 Hot-Rolled+Annealed+black Enquiry
1.2083 Forged Plate T:105-185mm*W:510*L Plate or Sheet Tons 26 Forged+QT Enquiry
X22CrMoV12-1 / 1.4923 Φ30mm Round Bar Kgs 300 Hot-Rolled+Annealed+black Enquiry
1.4882 strip/sheet/plate stock 3.5x200x1000-2000mm Coil or Strip Kgs 200 Cold-Rolled+Annealed Enquiry
A387 F5 & Grade 5 sheet Coil strip 0.5mmx200mmxC Coil or Strip Tons 3 Cold-Rolled+Annealed Enquiry
A387 F5 & Grade 5 Hot Coil stock Select Tons 3 Hot-Rolled+Annealed+black Enquiry
T45Cr5Si3 Round Bar Dia.40mm Round Bar Kgs 500 Hot-Rolled+Annealed+black Enquiry
UNS K30960(VIM+ESR) Bright Round Bar Dia.22mm Round Bar Kgs 50 Hot-Rolled+Annealed+black Enquiry
SA-437 Grade B4B/SUS 616 /422 Forged Bar Dia.160xL Round Bar Kgs 2120 Forged+QT Enquiry

Enquiry