ISO ISO NiCr15Fe7TiAl Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | ISO NiCr15Fe7TiAl | ISO | ISO |
Chemical composition % of the ladle analysis of grade ISO NiCr15Fe7TiAl
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | Al(%) | Other(%) |
|---|---|---|---|---|---|---|---|---|---|
| 0.03-0.10 | Max 0.50 | Max 0.50 | Max 0.015 | Max 0.015 | 14.0-17.0 | remaining | Max 0.15 | 1.10-1.35 | Fe:5.0-9.0,Nb+Ta 0.70-1.20 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 167 (≥) | 783 (≥) | 21 | 31 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 413 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 441 (≥) | 992 (≥) | 12 | 13 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 313 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 256 | 415 | 874 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| NiCr15Fe7TiAl | ISO | ISO | Heat-treatable steels, alloy steels and free-cutting steels -- Part 15: Valve steels for internal combustion engines |
| 2.4669 | ISO | ISO | NiCrFeTi alloy; High-temperature resisting material |
| NiCr15Fe7TiAl | ISO | ISO | NiCrFeTi alloy; High-temperature resisting material |
| N07750 | ISO | ISO | Ni-Cr Alloy Precipitation Hardenable |
| B 637 N07750 Type 1 | ISO | ISO | Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service |
| B 637 N07750 Type 2 | ISO | ISO | Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service |
| SB-637 N07750 Type 1 | ISO | ISO | Precipitation-Hardening Nickel Alloy Bars, Forgings, and Forging Stock for High-Temperature Service |
| Inconel X750 | ISO | ISO | Nickel Alloy, Corrosion and Heat-Resistant, Sheet, Strip, and Plate 72Ni - 15.5Cr - 0.95Cb(Nb) - 2.5Ti - 0.70Al - 7.0Fe Annealed |