ASTM T5 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | T5 | ASTM | USA |
Chemical composition % of the ladle analysis of grade T5
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | V(%) | W(%) | Co(%) |
|---|---|---|---|---|---|---|---|---|---|
| 0.75～0.85 | 0.20～0.40 | 0.20～0.40 | ≤0.030 | ≤0.030 | 3.75～5.00 | 0.50～1.25 | 1.80～2.40 | 17.5～19.0 | 7.00～9.50 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 395 (≥) | 581 (≥) | 11 | 31 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 341 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 768 (≥) | 979 (≥) | 14 | 14 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 122 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 125 | 984 | 296 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| Udimet 500 | ASTM | USA | Alloy Castings, Investment, Corrosion and Heat Resistant 53Ni - 18Cr - 18Co - 4.0Mo - 2.9Ti - 2.9Al - 0.006B Vacuum-Melted, Vacuum-Cast, Solution and Precipitation Heat Treated |
| Udimet 500 | ASTM | USA | Alloy Bars, Forgings, and Rings, Corrosion and Heat Resistant 54Ni - 17.5Cr - 16.5Co - 4.0Mo - 2.9Ti - 2.9Al - 0.006B Solution, Stabilization, and Precipitation Heat Treated Consumable Electrode or Vacuum Induction Melted |
| Udimet 500 | ASTM | USA | Alloy Castings, Investment, Corrosion and Heat Resistant 53Ni - 18Cr - 18Co - 4.0Mo - 2.9Ti - 2.9Al - 0.006B Vacuum-Melted, Vacuum-Cast, Solution and Precipitation Heat Treated |
| Udimet 500 | ASTM | USA | Alloy Bars, Forgings, and Rings, Corrosion and Heat Resistant 54Ni - 17.5Cr - 16.5Co - 4.0Mo - 2.9Ti - 2.9Al - 0.006B Solution, Stabilization, and Precipitation Heat Treated Consumable Electrode or Vacuum Induction Melted |
| Udimet 500 | ASTM | USA | Special Purpose Alloys ("Superalloys") |
| T51602 | ASTM | USA | Mold Steel |
| T51603 | ASTM | USA | Mold Steel |
| T51604 | ASTM | USA | Mold Steel |
| T51605 | ASTM | USA | Mold Steel |
| T51606 | ASTM | USA | Mold Steel |
| T51620 | ASTM | USA | Mold Steel |
| T51621 | ASTM | USA | Mold Steel |
| T5 | ASTM | USA | High-Speed Tool Steel |
| Z12CNDV12-03 | ASTM | USA | Iron and steel. Stainless steel for high temperature application |
| Z12CNDV12-03 | ASTM | USA | Iron and steel. Stainless steel for high temperature application |
| Z12CNDV12 Air 9160/C | ASTM | USA | wrought steels used in aeronautical constructions |