ISO X6CrMo17-1 Enquiry | Print this page
ISO X6CrMo17-1 Details
Stainless steels - Chemical composition
ISO X6CrMo17-1 Standard Download
X6CrMo17-1 Datasheet
ISO X6CrMo17-1| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | X6CrMo17-1 | Ferrite | International - ISO , ISO 15510 (2010) - Stainless steels -- Chemical composition ISO 16143-1 (2004) - Stainless steels for general purposes -- Part 1: Flat products ISO 4955 (2005) - Heat-resistant steels ISO 9328-7 (2011) - Steel flat products for pressure purposes - Technical delivery conditions - Part 7: Stainless steels ISO/TS 15510 (2003) - Stainless steels - Chemical composition |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.05 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | 0.040 | ||
| S | - | 0.030 | ||
| Cr | 16.00 | 19.00 | ||
| Ni | - | - | ||
| Mo | 0.90 | 1.40 | ||
| N | - | - | ||
| Ti | 4×(C+N)％+0.20 | 0.75 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 827 (≥) | 667 (≥) | 33 | 11 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 313 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 549 (≥) | 226 (≥) | 24 | 22 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 424 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 148 | 433 | 991 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X6CrMo17-1 | AWS | Germany | Steel rod, bars and steel wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels |
| 1.4113 | AWS | Germany | Steel rod, bars and steel wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels |
| X6CrMo17-1 | B.S. | UK | Steel rod, bars and steel wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels |
| 1.4113 | B.S. | UK | Steel rod, bars and steel wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels |
| X6CrMo17-1 | AFNOR | France | Steel rod, bars and steel wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels |
| 1.4113 | AFNOR | France | Steel rod, bars and steel wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels |
| X6CrMo17-1 | ISO | International | Stainless steels - Chemical composition |
| X6CrMo17-1 | ISO | International | Stainless steels - Chemical composition |
| X6CrMo17 1E | ISO | International | Steels for cold heading and cold extruding |