ISO X2CrNiMoN22-5-3 Enquiry | Print this page
ISO X2CrNiMoN22-5-3 Details
Stainless steels - Chemical composition
ISO X2CrNiMoN22-5-3 Standard Download
X2CrNiMoN22-5-3 Datasheet
ISO X2CrNiMoN22-5-3| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | X2CrNiMoN22-5-3 | Austenitic-Ferritic(Duplex steel) | International - ISO , ISO 15510 (2010) - Stainless steels -- Chemical composition ISO 16143-1 (2004) - Stainless steels for general purposes -- Part 1: Flat products ISO 16143-2 (2004) - Stainless steels for general purposes -- Part 2: Semi-finished products, bars, rods and sections ISO 16143-3 (2005) - Stainless steels for general purposes -- Part 3: Wire ISO 9327-5 (1999) - Steel forgings and rolled or forged bars for pressure purposes - Technical delivery conditions - Part 5: Stainless steels ISO 9328-7 (2011) - Steel flat products for pressure purposes - Technical delivery conditions - Part 7: Stainless steels ISO/TS 15510 (2003) - Stainless steels - Chemical composition |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.03 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.035 | ||
| S | - | 0.015 | ||
| Cr | 21.00 | 23.00 | ||
| Ni | 4.50 | 6.50 | ||
| Mo | 2.50 | 3.50 | ||
| N | 0.10 | 0.22 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 321 (≥) | 543 (≥) | 14 | 31 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 211 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 913 (≥) | 343 (≥) | 21 | 31 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 133 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 736 | 417 | 847 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X2CrNiMoN22-5-3 | B.S. | UK | Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 2: Stainless steel |
| 1.4462 | B.S. | UK | Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 2: Stainless steel |
| X2CrNiMoN22-5-3 | AFNOR | France | Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 2: Stainless steel |
| 1.4462 | AFNOR | France | Seamless circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 2: Stainless steel |
| X2CrNiMoN22-5-3 | ISO | International | Stainless steels - Chemical composition |