B.S. HR40 Details
Specification for cobalt-chromium-tungsten-nickel-manganese heat-resisting alloy billets, bars and forgings (cobalt base Cr 20, W 15, Ni 10, Mn 1.5)
B.S. HR40 Standard Download
HR40 Datasheet
B.S. HR40| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | HR40 | UK - B.S. , BS HR 40 (1972) - Specification for cobalt-chromium-tungsten-nickel-manganese heat-resisting alloy billets, bars and forgings (cobalt base, Cr 20, W 15, Ni 10, Mn 1.5) BS 2HR 40 (2010) - Specification for cobalt-chromium-tungsten-nickel-manganese heat-resisting alloy billets, bars and forgings (cobalt base Cr 20, W 15, Ni 10, Mn 1.5) |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.05 | 0.15 | ||
| Si | - | 0.40 | ||
| Mn | 1.00 | 2.00 | ||
| P | - | 0.040 | ||
| S | - | 0.030 | ||
| Cr | 19.00 | 21.00 | ||
| Ni | 9.00 | 11.00 | ||
| Mo | - | - | ||
| Co | - | remaining | ||
| Ti | - | - | ||
| Fe | - | 3.00 | ||
| W | 14.00 | 16.00 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 672 (≥) | 691 (≥) | 33 | 32 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 431 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 493 (≥) | 411 (≥) | 32 | 13 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 214 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 718 | 812 | 566 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| HR40 | B.S. | UK | Specification for cobalt-chromium-tungsten-nickel-manganese heat-resisting alloy billets, bars and forgings (cobalt base Cr 20, W 15, Ni 10, Mn 1.5) |
| 2HR401 | B.S. | UK | Specification for nickel-chromium-titanium-aluminium heat-resisting alloy seamless tubes (Nickel base, Cr 19.5, Ti 2.2, Al 1.4) |
| HR402 | B.S. | UK | Specification for nickel-chromium-cobalt-titanium-aluminium heat-resisting alloy seamless tubes (Nickel base, Cr 19.5, Co 18.0, Ti 2.5, Al 1.5) |
| HR403 | B.S. | UK | Specification for nickel-chromium-titanium heat-resisting alloy cold-worked and softened seamless tubes (nickel base, Cr 19.5, Ti 0.4) |
| HR404 | B.S. | UK | Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5) |