B.S. HR10 Enquiry | Print this page
B.S. HR10 Details
Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy billets, bars, forgings and parts (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)
B.S. HR10 Standard Download
HR10 Datasheet
B.S. HR10| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | HR10 | UK - B.S. , BS HR 10 (1972) - Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy billets, bars, forgings and parts (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5) BS 2HR 10 (2010) - Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy billets, bars, forgings and parts (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5) |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.04 | 0.08 | ||
| Si | 0.40 | - | ||
| Mn | 0.60 | - | ||
| P | - | - | ||
| S | - | 0.007 | ||
| Cr | 19.00 | 21.00 | ||
| Ni | - | remaining | ||
| Mo | 5.60 | 6.10 | ||
| Co | 19.00 | 21.00 | ||
| Ti | 1.90 | 2.40 | ||
| Fe | - | 0.70 | ||
| Al | 0.30 | 0.60 | ||
| Al+Ti | 2.40 | 2.80 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 857 (≥) | 336 (≥) | 23 | 23 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 111 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 442 (≥) | 623 (≥) | 33 | 22 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 422 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 571 | 853 | 615 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| HR10 | B.S. | UK | Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy billets, bars, forgings and parts (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5) |
| HR10 | B.S. | UK | Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy billets, bars, forgings and parts (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5) |