B.S. 6S.80 Enquiry | Print this page
B.S. 6S.80 Details
Specification for high chromium-nickel corrosion-resisting steel forging stock, bars, forgings and parts (880-1080 MPa, limiting ruling section 100 mm)
B.S. 6S.80 Standard Download
6S.80 Datasheet
B.S. 6S.80| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | 6S.80 | UK - B.S. , BS 6S 80 - Specification for high chromium-nickel corrosion-resisting steel forging stock, bars, forgings and parts (880-1080 MPa, limiting ruling section 100 mm) |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.12 | 0.20 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | 0.030 | ||
| S | - | 0.025 | ||
| Cr | 15.00 | 18.00 | ||
| Ni | 2.00 | 3.00 | ||
| Mo | - | 0.30 | ||
| Nb | - | 0.05 | ||
| Ti | - | 0.05 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 336 (≥) | 874 (≥) | 34 | 12 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 141 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 679 (≥) | 985 (≥) | 34 | 24 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 231 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 782 | 928 | 812 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 6S.80 | B.S. | UK | Specification for high chromium-nickel corrosion-resisting steel forging stock, bars, forgings and parts (880-1080 MPa, limiting ruling section 100 mm) |