AISI H15410 Enquiry | Print this page
AISI H15410 Details
Intake valve steel
AISI H15410 Standard Download
H15410 Datasheet
AISI H15410| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | H15410 | USA - AISI , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.42 | 0.45 | ||
| Si | 0.15 | 0.30 | ||
| Mn | 1.25 | 1.75 | ||
| P | - | 0.040 | ||
| S | - | 0.05 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 298 (≥) | 956 (≥) | 31 | 31 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 314 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 272 (≥) | 727 (≥) | 21 | 22 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 469 | 412 | 444 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| H15410 | AISI | USA | Intake valve steel |