SAE A 565 S42200 Details
Martensitic Stainless Steel Bars for High-Temperature Service
SAE A 565 S42200 Standard Download
A 565 S42200 Datasheet
SAE A 565 S42200| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | A 565 S42200 | Martensite | USA - SAE , A 565/A 565M (2010) - Martensitic Stainless Steel Bars for High-Temperature Service |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.20 | 0.25 | ||
| Mn | 0.50 | 1.00 | ||
| Si | - | 0.50 | ||
| P | - | 0.025 | ||
| S | - | 0.025 | ||
| Cr | 11.00 | 12.50 | ||
| Ni | 0.50 | 1.00 | ||
| Mo | 0.90 | 1.25 | ||
| W | 0.90 | 1.25 | ||
| V | 0.20 | 0.30 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 428 (≥) | 823 (≥) | 13 | 23 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 214 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 275 (≥) | 599 (≥) | 41 | 43 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 214 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 239 | 188 | 624 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| A 176 S42200 | SAE | USA | Stainless and Heat-Resisting Chromium Steel Plate, Sheet, and Strip |
| A 565 S42200 | SAE | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| S42200 | AISI | USA | Martensitic Chromium Molybdenum Nickel Wolfram Stainless Steel (422) |
| 616 | SAE | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| A 959 Type 616 | SAE | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
| SUH 616 | JIS | Japan | Heat-resisting steel bars and wire rods |
| STR616 | KS | Korea | Heat - resisting steel bars |
| SUH616 | CNS | China | CNS standard heat resistant steel bar steel grade and chemical composition |
| SNCM 616 | JIS | Japan | Low-alloyed steels for machine structural use manufactured by hot rolling, hot forging and hot extruding |
| A 176 S42200 | SAE | USA | Stainless and Heat-Resisting Chromium Steel Plate, Sheet, and Strip |
| A 565 S42200 | SAE | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| S42200 | AISI | USA | Martensitic Chromium Molybdenum Nickel Wolfram Stainless Steel (422) |
| HNV8 | UNS | USA | Steel for intake valves |
Relevant products
A 565 S42200 Equivalent Grade Stock
| Steel grade | Dimension | Shape | Unit | Quantity | Delivery state | Query |
|---|---|---|---|---|---|---|
| SA-437 Grade B4B/SUS 616 /422 Forged Bar | Dia.160xL | Round Bar | Kgs | 2120 | Forged+QT | Enquiry |
| Stainless Steel 422 / Alloy 422 AMS 5655 UNS S42200/616/B4B Round Bar Stock | Select | 0 | Select | Enquiry |