SAE A 312 TP310HCb Enquiry | Print this page
SAE A 312 TP310HCb Details
Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes
SAE A 312 TP310HCb Standard Download
A 312 TP310HCb Datasheet
SAE A 312 TP310HCb| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | A 312 TP310HCb | Austenite | USA - SAE , A 312/A 312M (2012) - Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.04 | 0.10 | ||
| Si | - | 0.75 | ||
| Mn | - | 2.00 | ||
| P | - | 0.045 | ||
| S | - | 0.030 | ||
| Cr | 24.00 | 26.00 | ||
| Ni | 19.00 | 22.00 | ||
| Nb+Ta | - | 1.10 | ||
| Cu | - | 0.75 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 728 (≥) | 226 (≥) | 42 | 23 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 333 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 716 (≥) | 567 (≥) | 34 | 21 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 431 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 179 | 627 | 316 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 310HCb | UNS | USA | Specification for Cold-Worked Welded Austenitic Stainless Steel Pipe |
| A 213 TP310HCb | SAE | USA | Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| A 240 Type 310HCb | SAE | USA | Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
| A 249 TP310HCb | SAE | USA | Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes |
| A 312 TP310HCb | SAE | USA | Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes |
| A 943 TP310HCb | SAE | USA | Spray-Formed Seamless Austenitic Stainless Steel Pipes |
| A 959 Type 310HCb | SAE | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
| SA-213 TP310HCb | AMS | USA | Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes |
| SA-249 TP310HCb | AMS | USA | Specification for Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes |
| SA-312 TP310HCb | AMS | USA | Specification for Seamless and Welded Austenitic Stainless Steel Pipes |
| A 240 S31041 | SAE | USA | Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
| A 249 S31041 | SAE | USA | Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes |
| S31041 | AISI | USA | Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |
| SA-240 S31041 | AMS | USA | Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications |