The chemically stable and high-temperature resistant nickel and cobalt NiCr23Mo16Al is mainly used in the chemical industry, flue gas desulphurating plants, paper industry.
Our product range in NiCr23Mo16Al are tubes and pipes, fittings and flanges, accessories.
EN NiCr23Mo16Al Enquiry | Print this page
EN NiCr23Mo16Al Details
EN NiCr23Mo16Al Standard Download
NiCr23Mo16Al Datasheet
EN NiCr23Mo16Al| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Superalloys | NiCr23Mo16Al | European - EN , DIN EN 17744 - The chemically stable and high-temperature resistant nickel and cobalt alloy 2.4605 (alloy 59) is mainly used in the chemical industry, flue gas desulphurating plants, paper industry. |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.01 | ||
| Si | - | 0.10 | ||
| Mn | - | 0.50 | ||
| P | - | 0.025 | ||
| S | - | 0.015 | ||
| Cr | 22.00 | 24.00 | ||
| Ni | - | Bal | ||
| Al | 0.10 | 0.40 | ||
| Co | - | 0.30 | ||
| Cu | - | 0.50 | ||
| Fe | - | 1.50 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 166 (≥) | 778 (≥) | 22 | 14 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 292 (≥) | 684 (≥) | 23 | 22 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 311 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 119 | 318 | 547 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 2.4605 | DIN | Germany | The chemically stable and high-temperature resistant nickel and cobalt alloy 2.4605 (alloy 59) is mainly used in the chemical industry, flue gas desulphurating plants, paper industry. |
| Alloy 59 | ASTM | USA | The chemically stable and high-temperature resistant nickel and cobalt alloy 2.4605 (alloy 59) is mainly used in the chemical industry, flue gas desulphurating plants, paper industry. |
| NiCr23Mo16Al | EN | European | The chemically stable and high-temperature resistant nickel and cobalt alloy 2.4605 (alloy 59) is mainly used in the chemical industry, flue gas desulphurating plants, paper industry. |