ГОСТ 10Xl1H20T2P(ЭИ696A) Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | 10Xl1H20T2P(ЭИ696A) | ГОСТ | Russia |
Chemical composition % of the ladle analysis of grade 10Xl1H20T2P(ЭИ696A)
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(%) | B(%) | Al(%) | Ti(%) |
|---|---|---|---|---|---|---|---|---|---|---|
| Max 0.10 | Max 1.0 | Max 1.0 | Max 0.02 | Max 0.02 | 10.0-12.5 | 18.0-21.0 | Max 0.2 | Max 0.008 | Max 0.50 | 2.3-2.8 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 527 (≥) | 561 (≥) | 13 | 42 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 242 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 845 (≥) | 574 (≥) | 14 | 11 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 731 | 632 | 856 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 10Xl1H20T2P(ЭИ696A) | ГОСТ | Russia | Russia GOCT standard deformation of high temperature alloy grades and chemical composition |