GBT K403 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | K403 | GBT | China |
Chemical composition % of the ladle analysis of grade K403
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | W(%) | Co(%) | B(%) | Al(%) | Ti(%) | Other(%) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.11-0.18 | Max 0.5 | Max 0.5 | Max 0.02 | Max 0.01 | 10.0-12.0 | Balance | 3.80-4.50 | 4.80-5.50 | 4.50-6.00 | 0.012-0.022 | 5.30-5.90 | 2.30-2.90 | Ce:Max 0.01,Zr: 0.03-0.08 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 375 (≥) | 787 (≥) | 24 | 22 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 244 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 313 (≥) | 568 (≥) | 13 | 13 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 563 | 153 | 712 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |