EN EN NiCr22Fe18Mo Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | EN NiCr22Fe18Mo | EN | Euronorm |
Chemical composition % of the ladle analysis of grade EN NiCr22Fe18Mo
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) |
|---|---|---|---|---|---|---|
| 0.05-0.15 | 1.00 | 1.00 | 0.020 | 0.015 | 20.5-23.0 | 8.00-10.0 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 973 (≥) | 661 (≥) | 44 | 21 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 231 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 131 (≥) | 978 (≥) | 43 | 32 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 973 | 394 | 512 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH 3536 | EN | Euronorm | Superalloy GH536 is a kind of added tungsten cobalt and nickel - chromium - molybdenum alloy.GH536 alloy at 1200 ℃ with excellent oxidation resistance at high temperature, also can be applied to the neutral and reducing atmosphere.At the same time GH536 a |