GBT 20Mn Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | 20Mn | GBT | China |
Chemical composition % of the ladle analysis of grade 20Mn
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(%) |
|---|---|---|---|---|---|---|---|
| 0.17-0.23 | 0.17-0.37 | 0.70-1.00 | 0.035 | 0.035 | 0.25 | 0.3 | 0.25 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 679 (≥) | 883 (≥) | 43 | 44 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 142 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 117 (≥) | 491 (≥) | 42 | 44 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 233 | 892 | 432 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 2Cr20Mn9Ni2Si2N | GBT | China | Heat-resisting steel bars |
| 1.3802 | GBT | China | Steel castings - Austenitic manganese steel castings |
| GX120Mn13 | GBT | China | Steel castings - Austenitic manganese steel castings |
| X120Mn12, 1.3401, A128, X110Mn14 | GBT | China | X120Mn12, 1.3401, A128, X110Mn14 High-manganese steels with austenitic structure, characterized by high carbon content - on average 1.00-1.20%, and high Manganese content - approx. |