STAS/SR R52 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | R52 | STAS/SR | Romania |
Chemical composition % of the ladle analysis of grade R52
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | V(%) | Cu(%) | Al(%) |
|---|---|---|---|---|---|---|---|---|
| Min 0.18 | 0.17-0.45 | 1.05-1.65 | 0.035 | 0.035 | Min 0.30 | Min 0.15 | 0.30 | Min 0.025 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 835 (≥) | 683 (≥) | 41 | 12 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 136 (≥) | 965 (≥) | 21 | 33 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 442 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 243 | 238 | 281 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| HR52 | STAS/SR | Romania | Specification for heat-resisting alloy billets, bars, forgings and parts (Ni 25.5, Cr 14.7, Ti 1.8, Mn 1.5, Mo 1.2, V 0.3, Fe remainder) |