SS 2368 Application:Swedish SS standard stainless steel and heat resistant steel

Category	Type	Steel grade	Standard	Country
Grades	Special Alloy	SS 2368	SS	Sweden

Chemical composition % of the ladle analysis of grade SS 2368

C(％)	Si(％)	Mn(％)	P(％)	S(％)	Cr(％)	Ni(％)	N(%)	Other(%)
0.05-0.10	1.4-2.0	Max 0.80	Max 0.04	Max 0.03	20.0-22.0	10.0-12.0	0.14-0.20	Ce 0.03-0.08

Swedish SS standard stainless steel and heat resistant steel

Mechanical properties of grade SS 2368

Proof strength Rp0.2 (MPa)	Tensile strength Rm (MPa)	Impact energy KV (J)	Elongation at fracture A (%)	Reduction in cross section on fracture Z (%)	As-Heat-Treated Condition	Brinell hardness (HBW)
217 (≥)	844 (≥)	34	41	31	Solution and Aging, Annealing, Ausaging, Q+T,etc	232

Physical properties of grade SS 2368

Property	Density kg/dm3	Temperature T °C/F	Specific heat J / kgK	Thermal conductivity W/mK	Electric resistance µΩ·cm	Modulus of elasticity kN/mm2	Expansion rate
475 (≥)	614 (≥)	44	43	14	Solution and Aging, Annealing, Ausaging, Q+T,etc	144
Temp. °C/°F	Creep strain limit (10000h) (Rp1,0) N/mm2	Creep rupture strength (10000h) (Rp1,0) N/mm2
622	286	332

SS 2368 Range of products

Product type	Products	Dimension	Processes	Deliver Status
Plates / Sheets	Plates / Sheets	0.08-200mm(T)*W*L	Forging, hot rolling and cold rolling	Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar	Round Bar, Flat Bar, Square Bar	Φ8-1200mm*L	Forging, hot rolling and cold rolling, Cast	Black, Rough Turning, Shot Blasting,
Coil / Strip	Steel Coil /Steel Strip	0.03-16.0x1200mm	Cold-Rolled & Hot-Rolled	Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes	Seamless Pipes/Tubes, Welded Pipes/Tubes	OD:6-219mm x WT:0.5-20.0mm	Hot extrusion, Cold Drawn, Welded	Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade	Standard	Country	Application
2368	SS	Sweden	Stainless steel - SS steel 2368