SS 2317 Application:Swedish SS standard stainless steel and heat resistant steel
Category Type Steel grade Standard Country
Grades Special Alloy SS 2317 SS Sweden

Chemical composition % of the ladle analysis of grade SS 2317

C(％) Si(％) Mn(％) P(％) S(％) Cr(％) Ni(％) Mo(％) V(%)
0.18-0.24 0.10-0.50 0.30-0.80 Max 0.035 Max 0.035 11.0-12.5 0.30-0.80 0.80-1.20 0.25-0.35
Swedish SS standard stainless steel and heat resistant steel
Mechanical properties of grade SS 2317
Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
929 (≥) 886 (≥) 44 31 33 Solution and Aging, Annealing, Ausaging, Q+T,etc 421
Physical properties of grade SS 2317
Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
488 (≥) 275 (≥) 22 23 14 Solution and Aging, Annealing, Ausaging, Q+T,etc 143
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
742 844 483
SS 2317 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
2317 SS Sweden
High-strength, high-temperature martensitic steel