ISO ISO H14 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | ISO H14 | ISO | ISO |
Chemical composition % of the ladle analysis of grade ISO H14
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) |
|---|---|---|---|---|---|---|
| Max 0.08 | Max 1.0 | Max 2.0 | Max 0.045 | Max 0.030 | 22.0-24.0 | 12.0-15.0 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 948 (≥) | 622 (≥) | 34 | 12 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 433 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 515 (≥) | 357 (≥) | 31 | 42 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 323 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 482 | 627 | 169 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| S14800 | ISO | ISO | Precipitation Hardenable Chromium Nickel Molybdenum Aluminum Stainless Steel |
| S14800 | ISO | ISO | Precipitation Hardenable Chromium Nickel Molybdenum Aluminum Stainless Steel |
| PH 14-8 Mo | ISO | ISO | Sheet and Strip 15Cr - 8,4Ni - 2,2Mo - 1,1Al, vac. Induct. Melted, Solution Heat Treated |
| PH 14-8 Mo | ISO | ISO | Sheet and Strip 15Cr - 8,4Ni - 2,2Mo - 1,1Al, vac. Induct. Melted, Solution Heat Treated |
| 08X20H14C2 | ISO | ISO | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 20X20H14C2 | ISO | ISO | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 45X14H1482M | ISO | ISO | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 03X17H14M2 | ISO | ISO | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 06X20H14C2 | ISO | ISO | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 12X20H14C2 | ISO | ISO | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| 45X14H14CB2M | ISO | ISO | Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition |
| ISO H14 | ISO | ISO | Heat-resistant steels |
| H14 | ISO | ISO | Hot-Work Tool Steel |
| H14 | ISO | ISO | Hot-Work Tool Steel |