ISO ISO X2CrNiMo17-13 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | ISO X2CrNiMo17-13 | ISO | ISO |
Chemical composition % of the ladle analysis of grade ISO X2CrNiMo17-13
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) |
|---|---|---|---|---|---|---|---|
| Max 0.030 | Max 1.00 | Max 2.00 | Max 0.040 | Max 0.030 | 16.5-18.5 | 2.50-3.00 | 11.5-14.5 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 569 (≥) | 469 (≥) | 44 | 33 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 964 (≥) | 452 (≥) | 42 | 34 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 242 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 491 | 758 | 263 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X2CrNiMo17-12-2 | ISO | ISO | DIN 1654-5 (1989) Cold heading and cold extruding steels; technical delivery conditions for stainless steels; Replaced by DIN EN 10263-5:2002 |
| 1.4404 | ISO | ISO | DIN 1654-5 (1989) Cold heading and cold extruding steels; technical delivery conditions for stainless steels; Replaced by DIN EN 10263-5:2002 |
| X2CrNiMo17-13-2 | ISO | ISO | DIN 1654-5 (1989) Cold heading and cold extruding steels; technical delivery conditions for stainless steels; Replaced by DIN EN 10263-5:2002 |
| X2CrNiMo17-13 3E | ISO | ISO | Steels for cold heading and cold extruding |
| X2CrNiMo17-13 | ISO | ISO | Welded steel tubes for pressure purposes - Technical delivery conditions - Part 6: Longitudinally welded austenitic stainless steel tubes |
| X2CrNiMo17-13 | ISO | ISO | Welded steel tubes for pressure purposes - Technical delivery conditions - Part 6: Longitudinally welded austenitic stainless steel tubes |