X19CrNi16 2E Application:ISO standard cold and cold extrusion stainless steel
Category Type Steel grade Standard Country
Grades Special Alloy X19CrNi16 2E ISO ISO

Chemical composition % of the ladle analysis of grade X19CrNi16 2E

C(％) Si(％) Mn(％) P(％) S(％) Cr(％) Ni(％) Nb(%)
0.14-0.23 Max 1.00 Max 1.00 Max 0.040 Max 0.030 15.0-17.5 1.5-2.5 6xC％-1.00
ISO standard cold and cold extrusion stainless steel
Mechanical properties of grade X19CrNi16 2E
Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
394 (≥) 984 (≥) 21 44 21 Solution and Aging, Annealing, Ausaging, Q+T,etc 144
Physical properties of grade X19CrNi16 2E
Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
113 (≥) 599 (≥) 14 42 22 Solution and Aging, Annealing, Ausaging, Q+T,etc 343
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
317 353 527
X19CrNi16 2E Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
X19CrNi16 2E ISO ISO
Steels for cold heading and cold extruding