AISI CZ-3 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | CZ-3 | AISI | USA |
Chemical composition % of the ladle analysis of grade CZ-3
| C(％) | W(%) | Co(%) | Ti(%) | Ta(%) |
|---|---|---|---|---|
| 7.30 | 70.41 | 8.0 | 9.60 | 4.69 |
Physical and mechanical performance | density g/cm ^ 3:11.80
Physical and mechanical performance | hardness HRC: 91.5
Physical and mechanical performance | σ bb MPa: 1160 ~ 1580
Physical and mechanical performance | grain size μ m: 2 ~ 3
Use for example: used for light load of steel finish machining (toughness is CZ-2 high)
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 698 (≥) | 277 (≥) | 11 | 22 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 231 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 391 (≥) | 223 (≥) | 32 | 43 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 411 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 572 | 192 | 114 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |