AISI CU-2 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | CU-2 | AISI | USA |
Chemical composition % of the ladle analysis of grade CU-2
| C(％) | W(%) | Co(%) | Nb(%) | Ta(%) |
|---|---|---|---|---|
| 5.8 | 86.3 | 5.8 | 0.3 | 1.8 |
Density / (g/cm ^ 3) : 14.80
Hardness HRC: 92.0
σ bb/MPa: 1760
Grain size/μ m: 2 ~ 3
Use for example: can be used to cast iron and the iron materials and half of the rough finished finishing
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 417 (≥) | 912 (≥) | 13 | 24 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 334 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 776 (≥) | 713 (≥) | 12 | 11 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 142 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 273 | 668 | 157 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |