UNS T12008 Enquiry | Print this page

T12008 Application:Tungsten series High-Speed Tool Steel
Category Type Steel grade Standard Country
Grades Special Alloy T12008 UNS USA

Chemical composition % of the ladle analysis of grade T12008

C(％) Si(％) Mn(％) P(％) S(％) Cr(％) Mo(％) V(%) W(%) Co(%)
0.75～0.85 0.20～0.40 0.20～0.40 ≤0.030 ≤0.030 3.75～4.50 0.40～1.00 1.80～2.40 13.25～14.75 4.25～5.75
T12008
Mechanical properties of grade T12008
Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
361 (≥) 168 (≥) 43 11 32 Solution and Aging, Annealing, Ausaging, Q+T,etc 231
Physical properties of grade T12008
Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
846 (≥) 468 (≥) 12 31 43 Solution and Aging, Annealing, Ausaging, Q+T,etc 414
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
576 697 714
T12008 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
T12008 UNS USA
High-Speed Tool Steel