DIN X5CrNiCuNb16-4 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | X5CrNiCuNb16-4 | DIN | Germany |
Chemical composition % of the ladle analysis of grade X5CrNiCuNb16-4
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(%) | Nb(%) |
|---|---|---|---|---|---|---|---|---|
| Max 0.07 | Max 0.70 | Max 1.50 | Max 0.040 | Max 0.015② | 15.0-17.0 | 3.00-5.00 | 3.00-5.00 | 5×C％Max 0.45 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 746 (≥) | 539 (≥) | 14 | 44 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 295 (≥) | 685 (≥) | 24 | 12 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 971 | 888 | 989 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X5CrNiCuNb16-4 | DIN | Germany | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| 1.4542 | DIN | Germany | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| X5CrNiCuNb16-4 | DIN | Germany | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| 1.4542 | DIN | Germany | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| X5CrNiCuNb16-4 | DIN | Germany | Stainless steels - Chemical composition |
| 17-4PH, 1.4542, X5CrNiCuNb16-4 | DIN | Germany | Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4) |