UNS S13800 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | S13800 | UNS | USA |
Chemical composition % of the ladle analysis of grade S13800
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | N(%) | Al(%) |
|---|---|---|---|---|---|---|---|---|---|
| 0.05 | 0.1 | 0.2 | Max 0.01 | Max 0.008 | 12.25-13.5 | 7.50-8.50 | 7.50-8.50 | 0.01 | 0.90-1.35 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 178 (≥) | 986 (≥) | 24 | 33 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 433 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 996 (≥) | 739 (≥) | 11 | 24 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 342 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 885 | 118 | 251 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| A 564 S13800 | UNS | USA | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
| A 693 S13800 | UNS | USA | Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip |
| A 705 S13800 | UNS | USA | Age-Hardening Stainless Steel Forgings |
| S13800 | UNS | USA | Precipitation Hardenable Chromium Nickel Aluminum Molybdenum Stainless Steel |
| SA-564 S13800 | UNS | USA | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
| SA-693 S13800 | UNS | USA | Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip |
| SA-705 S13800 | UNS | USA | Specification for Age-Hardening Stainless Steel Forgings |
| A 564 S13800 | UNS | USA | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
| A 693 S13800 | UNS | USA | Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip |
| A 705 S13800 | UNS | USA | Age-Hardening Stainless Steel Forgings |
| S13800 | UNS | USA | Precipitation Hardenable Chromium Nickel Aluminum Molybdenum Stainless Steel |
| SA-564 S13800 | UNS | USA | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
| SA-693 S13800 | UNS | USA | Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip |
| SA-705 S13800 | UNS | USA | Specification for Age-Hardening Stainless Steel Forgings |
| A 564 XM-13 | UNS | USA | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
| A 693 Type XM-13 | UNS | USA | Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip |
| A 705 XM-13 | UNS | USA | Age-Hardening Stainless Steel Forgings |
| A 959 Type XM-13 | UNS | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
| F 899 Type XM-13 | UNS | USA | Standard Specification for Wrought Stainless Steels for Surgical Instruments |
| SA-564 XM-13 | UNS | USA | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |