ASTM S6 Enquiry | Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | S6 | ASTM | USA |
Chemical composition % of the ladle analysis of grade S6
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | V(%) |
|---|---|---|---|---|---|---|---|
| 0.40～0.50 | 2.00～2.50 | 1.20～1.50 | ≤0.030 | ≤0.030 | 1.20～1.50 | 0.30～0.50 | 0.20～0.40 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 565 (≥) | 716 (≥) | 13 | 32 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 341 (≥) | 782 (≥) | 12 | 13 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 233 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 822 | 634 | 851 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| S63198 | ASTM | USA | Iron Base Superalloy |
| S66220 | ASTM | USA | Iron Base Superalloy |
| A 959 S66286 | ASTM | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
| S66286 | ASTM | USA | Iron Base Superalloy |
| S63198 | ASTM | USA | Iron Base Superalloy |
| HNVl | ASTM | USA | Steel for intake valves |
| S64005 | ASTM | USA | Steel for intake valves |
| HNV2 | ASTM | USA | Steel for intake valves |
| S64006 | ASTM | USA | Steel for intake valves |
| HNV3 | ASTM | USA | Steel for intake valves |
| S65007 | ASTM | USA | Steel for intake valves |
| HNV5 | ASTM | USA | Steel for intake valves |
| S63005 | ASTM | USA | Steel for intake valves |
| HNV6 | ASTM | USA | Steel for intake valves |
| S65006 | ASTM | USA | Steel for intake valves |
| EV3 | ASTM | USA | Steel for exhaust valves |
| S63016 | ASTM | USA | Steel for exhaust valves |
| EV4 | ASTM | USA | Steel for exhaust valves |
| S63017 | ASTM | USA | Steel for exhaust valves |
| EV5 | ASTM | USA | Steel for exhaust valves |
Relevant products
S6 Equivalent Grade Stock
| Steel grade | Dimension | Shape | Unit | Quantity | Delivery state | Query |
|---|---|---|---|---|---|---|
| SA-437 Grade B4B/SUS 616 /422 Forged Bar | Dia.160xL | Round Bar | Kgs | 2120 | Forged+QT | Enquiry |