Location » Home » Grades > Cast Iron and Cast Steel > F10011

AISI F10011 Details

F10011

AISI F10011 Standard Download

Tags

F10011 Application:Used in the products of the automobile, truck, tractor, and allied industries
Category Type Grade Microstructure Designations
Grades Cast Iron and Cast Steel F10011 Pearlitic USA - AISI , A 159 (2011) - Automotive Gray Iron Castings
Chemical composition(mass fraction)(wt.%)
Elements Min.(≥) Max.(≤) Similar Remarks
C - 3.50
Si 1.30 1.80
Mn 0.60 0.90
P - 0.15
S - 0.12
Mechanical properties of grade F10011
Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
273 (≥) 795 (≥) 43 21 21 Solution and Aging, Annealing, Ausaging, Q+T,etc 313
Physical properties of grade F10011
Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
732 (≥) 172 (≥) 33 41 31 Solution and Aging, Annealing, Ausaging, Q+T,etc 422
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
646 858 543
F10011 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
F10011 AISI USA
Used in the products of the automobile, truck, tractor, and allied industries