Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007)

Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007)

Austenitic stainless steel. Grade 00Cr17Ni14Mo2 was replaced by new designation 022Cr17Ni12Mo2 according to GB/T 20878 (2007)

Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes

Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes

Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes

Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes

Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes

Seamless stainless steel tubes for boiler and heat exchanger

Seamless stainless steel tubes for boiler and heat exchanger

Seamless stainless steel tubes for boiler and heat exchanger

Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel

Corrosion resistance and heat resistance are better than 0cr19ni9

Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading

In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance

Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES

Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components

Nickel steel, instead of 1cr18ni9

Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc

Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts

Seamless stainless steel tubes for boiler and heat exchanger

Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws

High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc

Of urea with good corrosion resistance, can produce urea corrosion of the equipment.

High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts

Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut